KLUBERSYNTH GH 6

Synthetic gear and high temperature oils with KlüberComp Lube Technology.

Klüberoil 4 UH1 N is a polyalphaolefin-based, high-performance multi-purpose oil and gear oil that can meet the increasing power density and increasing requirements of modern gears. Klüberoil 4 UH1 N contains high-level raw materials and improved additives that provide maximum performance in the lubrication of gear equipment.

Klübersynth GH 6 clearly exceeds the CLP requirements according to DIN 51517-3. Klüberoil 4 UH 1 N can be used in relevant gears without consulting the gear manufacturers, observing the general application notes.

Klübersynth GH 6 offers the high friction load capacity of API GL-5 if ISO VG 220 or higher is selected. The gears are effectively protected against wear even under extreme sudden loads, vibration and oscillation or in the absence of break-in lubrication. The excellent wear protection of both gears and rolling bearings ensures the calculated service life of the lubricated components, reducing maintenance and repair costs. The oil's high micropitting resistance GFT ≥ 10 according to FVA 54/7 (tested at 90, 60 and 40 °C) provides adequate protection for gears subjected to high loads and normally susceptible to such damage.

Klüberoil 4 UH 1 N offers a much longer working life than mineral oils and white oils, thanks to the excellent aging and oxidation resistance of selected base oils; Thus, service intervals can be extended and maintenance costs can be reduced. Its low foaming tendency and anti-corrosion properties ensure trouble-free gear operation. The product's low foaming tendency and anti-rust properties ensure trouble-free gear operation. Freudenberg seals made of 72 NBR 902 (exception: ISO VG 22), 75 FKM 585, 75 FKM 260466 and 75 FKM 170055

It is statically and dynamically resistant to Klübersynth GH 6. Leakage and contamination are prevented. Therefore, a single viscosity range can cover low and high temperatures in many applications. Therefore, a single viscosity grade can handle both low and high temperatures in many applications.

The optimized friction behavior provided by carefully selected base oils reduces power loss and increases gear efficiency. Thanks to optimized additives, wear values are reduced and a very low wear intensity is achieved according to DIN 3996 (calculation of the load capacity of worm gears).

Klübersynth GH 6 Flender, Siemens, Siemens Geared Motors, SEW Eurodrive, Getriebebau Nord, Stöber Antriebstechnik, Lenze, ZAE Antriebssysteme, Cavex, Bonfiglioli, Rossi Motoriduttori, Motovario, Moventas, Boston Gear, Baldor, Yilmaz Redüktör etc. Approved by.

Klübersynth GH 6 oils have been specially developed for the lubrication of worm gears running in steel/bronze or steel/grey cast iron.
Klübersynth GH 6 oils are used for the lubrication of bevel and spur gears, bearings and plain bearings, as well as all gear couplings, especially those exposed to high temperatures.
It is also used to lubricate lifting, drive and conveyor chains.

Provides high abrasion protection.
Provides excellent wear protection for gears and bearings.
It provides safe lubrication film formation thanks to its good dynamic viscosity.
It shows high micropitting resistance.
Provides optimum lubrication for worm gears.
It offers excellent aging and oxidation resistance.
It offers a wide operating temperature range thanks to its good viscosity-temperature behavior.
It has a low tendency to foam.
It saves energy thanks to its optimized friction behavior.
Elastomer compatibility is good.
Approved by numerous gear manufacturers.

Ürün Bilgisi	Klübersynth GH 6-22	Klübersynth GH 6-32	Klübersynth GH 6-46	Klübersynth GH 6-80
Artikel Numarası	012287	012157	012009	012158
Çalışma Sıcaklığı, Alt Limit	-55 °C	-45 °C	-40 °C	-40 °C
Çalışma Sıcaklığı, Üst Limit	160 °C	160 °C	160 °C	160 °C
Tanım, DIN 51502	-	CLP PG 32	CLP PG 46	CLP PG 80
Tanım, ISO 12925-1	-	CKC 32	CKC 46	CKC 80
Yoğunluk, DIN 51757, 15°C	Yaklaşık 1025 kg/m³	Yaklaşık 984 kg/m³	Yaklaşık 1035 kg/m³	Yaklaşık 1040 kg/m³
Parlama Noktası, DIN EN ISO 2592, Cleveland, Açık Kap	≥ 165 °C	≥ 180 °C	≥ 180 °C	≥ 220 °C
Köpük Testi, ISO 6247 / ASTM D892, 24°C, Adım I	≤ 100/10 ml	≤ 100/10 ml	≤ 100/10 ml	≤ 100/10 ml
Köpük Testi, ISO 6247 / ASTM D892, 24°C, Adım III	≤ 100/10 ml	≤ 100/10 ml	≤ 100/10 ml	≤ 100/10 ml
Köpük Testi, ISO 6247 / ASTM D892, 93.5°C, Adım II	≤ 100/10 ml	≤ 100/10 ml	≤ 100/10 ml	≤ 100/10 ml
ISO Viskozite Sınıfı, DIN ISO 3448, ISO VG	22	32	46	80
Kinematik Viskozite, DIN EN ISO 3104 / DIN 51562-1 / ASTM D445 / ASTM D7042, 100°C	Yaklaşık 5.3 mm²/s	Yaklaşık 6.5 mm²/s	Yaklaşık 9 mm²/s	Yaklaşık 14.5 mm²/s
Kinematik Viskozite, DIN EN ISO 3104 / DIN 51562-1 / ASTM D445 / ASTM D7042, 20°C	Yaklaşık 54 mm²/s	Yaklaşık 88 mm²/s	Yaklaşık 113 mm²/s	Yaklaşık 205 mm²/s
Kinematik Viskozite, DIN EN ISO 3104 / DIN 51562-1 / ASTM D445 / ASTM D7042, 40°C	Yaklaşık 22 mm²/s	Yaklaşık 32 mm²/s	Yaklaşık 46 mm²/s	Yaklaşık 68 mm²/s
Viskozite İndeksi, DIN ISO 2909	≥ 150	≥ 150	≥ 190	≥ 190
Bakır Korozyonu, DIN EN ISO 2160, 24 hours, 100°C	1 - 100 - 24 Korozyon Derecesi	1 - 100 - 24 Korozyon Derecesi	1 - 100 - 24 Korozyon Derecesi	1 - 100 - 24 Korozyon Derecesi
Çelik Korozyonu, DIN ISO 7120 / ASTM D665, Yöntem A, 24 Hours, 60°C	Pas Yok	Pas Yok	Pas Yok	Pas Yok
Akma Noktası, DIN ISO 3016	≤ -55 °C	≤ -45 °C	≤ -40 °C	≤ -40 °C
Yaşlanma Davranışı, DIN EN ISO 4263-4 / ASTM D2893, 312 Hours, 95°C, 100°C'de Viskozitede Artış	≤ 6 %	≤ 6 %	≤ 6 %	≤ 6 %
API Aşındırma Yük Kademesi	-	-	-	-
FAG FE8 Rulman Testi, DIN 51819-3, D-7.5 / 80-80, Kafes Aşınması	≤ 200 mg	≤ 200 mg	≤ 200 mg	≤ 200 mg
FAG FE8 Rulman Testi, DIN 51819-3, D-7.5 / 80-80, Rulman Aşınması	< 5 mg	< 5 mg	< 5 mg	< 5 mg
FZG Aşındırma Testi, DIN ISO 14635-1, Based on Standard, A / 16.6 / 90, Başarısız Yük Kademesi	≥ 12	≥ 12	≥ 12	≥ 12
FZG Aşındırma Testi, DIN ISO 14635-1, A / 8.3 / 90, Başarısız Yük Kademesi	≥ 14	≥ 14	≥ 14	≥ 14
Üretim Tarihinden İtibaren Minimum Raf Ömrü – Açılmamış Orijinal Ambalajında, Serin ve Kuru Yerde, Yaklaşık	36 Ay	36 Ay	36 Ay	36 Ay

Ürün Bilgisi	Klübersynth GH 6-100	Klübersynth GH 6-150	Klübersynth GH 6-220	Klübersynth GH 6-320
Artikel Numarası	012159	012160	012161	012162
Çalışma Sıcaklığı, Alt Limit	-35 °C	-35 °C	-35 °C	-30 °C
Çalışma Sıcaklığı, Üst Limit	160 °C	160 °C	160 °C	160 °C
Tanım, DIN 51502	CLP PG 100	CLP PG 150	CLP PG 220	CLP PG 320
Tanım, ISO 12925-1	CKC 100	CKC 150	CKC 220	CKC 320
Yoğunluk, DIN 51757, 15°C	Yaklaşık 1043 kg/m³	Yaklaşık 1050 kg/m³	Yaklaşık 1060 kg/m³	Yaklaşık 1067 kg/m³
Parlama Noktası, DIN EN ISO 2592, Cleveland, Açık Kap	≥ 250 °C	≥ 250 °C	≥ 250 °C	≥ 250 °C
Köpük Testi, ISO 6247 / ASTM D892, 24°C, Adım I	≤ 100/10 ml	≤ 100/10 ml	≤ 100/10 ml	≤ 100/10 ml
Köpük Testi, ISO 6247 / ASTM D892, 24°C, Adım III	≤ 100/10 ml	≤ 100/10 ml	≤ 100/10 ml	≤ 100/10 ml
Köpük Testi, ISO 6247 / ASTM D892, 93.5°C, Adım II	≤ 100/10 ml	≤ 100/10 ml	≤ 100/10 ml	≤ 100/10 ml
ISO Viskozite Sınıfı, DIN ISO 3448, ISO VG	100	150	220	320
Kinematik Viskozite, DIN EN ISO 3104 / DIN 51562-1 / ASTM D445 / ASTM D7042, 100°C	Yaklaşık 20 mm²/s	Yaklaşık 29 mm²/s	Yaklaşık 40 mm²/s	Yaklaşık 54 mm²/s
Kinematik Viskozite, DIN EN ISO 3104 / DIN 51562-1 / ASTM D445 / ASTM D7042, 20°C	Yaklaşık 270 mm²/s	Yaklaşık 400 mm²/s	Yaklaşık 630 mm²/s	Yaklaşık 880 mm²/s
Kinematik Viskozite, DIN EN ISO 3104 / DIN 51562-1 / ASTM D445 / ASTM D7042, 40°C	Yaklaşık 100 mm²/s	Yaklaşık 150 mm²/s	Yaklaşık 220 mm²/s	Yaklaşık 320 mm²/s
Viskozite İndeksi, DIN ISO 2909	≥ 190	≥ 210	≥ 220	≥ 230
Bakır Korozyonu, DIN EN ISO 2160, 24 hours, 100°C	1 - 100 - 24 Korozyon Derecesi	1 - 100 - 24 Korozyon Derecesi	1 - 100 - 24 Korozyon Derecesi	1 - 100 - 24 Korozyon Derecesi
Çelik Korozyonu, DIN ISO 7120 / ASTM D665, Yöntem A, 24 Hours, 60°C	Pas Yok	Pas Yok	Pas Yok	Pas Yok
Akma Noktası, DIN ISO 3016	≤ -40 °C	≤ -35 °C	≤ -35 °C	≤ -30 °C
Yaşlanma Davranışı, DIN EN ISO 4263-4 / ASTM D2893, 312 Hours, 95°C, 100°C'de Viskozitede Artış	≤ 6 %	≤ 6 %	≤ 6 %	≤ 6 %
API Aşındırma Yük Kademesi	-	-	API GL 5	API GL 5
FAG FE8 Rulman Testi, DIN 51819-3, D-7.5 / 80-80, Kafes Aşınması	≤ 200 mg	≤ 200 mg	≤ 200 mg	≤ 200 mg
FAG FE8 Rulman Testi, DIN 51819-3, D-7.5 / 80-80, Rulman Aşınması	< 5 mg	< 5 mg	< 5 mg	< 5 mg
FZG Aşındırma Testi, DIN ISO 14635-1, Based on Standard, A / 16.6 / 90, Başarısız Yük Kademesi	≥ 12	≥ 12	≥ 12	≥ 12
FZG Aşındırma Testi, DIN ISO 14635-1, A / 8.3 / 90, Başarısız Yük Kademesi	≥ 14	≥ 14	≥ 14	≥ 14
Üretim Tarihinden İtibaren Minimum Raf Ömrü – Açılmamış Orijinal Ambalajında, Serin ve Kuru Yerde, Yaklaşık	36 Ay	36 Ay	36 Ay	36 Ay

Ürün Bilgisi	Klübersynth GH 6-460	Klübersynth GH 6-680	Klübersynth GH 6-1000	Klübersynth GH 6 1500
Artikel Numarası	012163	012164	012165	012281
Çalışma Sıcaklığı, Alt Limit	-25 °C	-25 °C	-25 °C	-10 °C
Çalışma Sıcaklığı, Üst Limit	160 °C	160 °C	160 °C	160 °C
Tanım, DIN 51502	CLP PG 460	CLP PG 680	CLP PG 1000	CLP PG 1500
Tanım, ISO 12925-1	CKC 460	CKC 680	CKC 1000	CKC 1500
Yoğunluk, DIN 51757, 15°C	Yaklaşık 1074 kg/m³	Yaklaşık 1075 kg/m³	Yaklaşık 1075 kg/m³	Yaklaşık 1080 kg/m³
Parlama Noktası, DIN EN ISO 2592, Cleveland, Açık Kap	≥ 250 °C	≥ 250 °C	≥ 250 °C	≥ 250 °C
Köpük Testi, ISO 6247 / ASTM D892, 24°C, Adım I	≤ 100/10 ml	≤ 100/10 ml	≤ 100/10 ml	≤ 100/10 ml
Köpük Testi, ISO 6247 / ASTM D892, 24°C, Adım III	≤ 100/10 ml	≤ 100/10 ml	≤ 100/10 ml	≤ 100/10 ml
Köpük Testi, ISO 6247 / ASTM D892, 93.5°C, Adım II	≤ 100/10 ml	≤ 100/10 ml	≤ 100/10 ml	≤ 100/10 ml
ISO Viskozite Sınıfı, DIN ISO 3448, ISO VG	460	680	1000	1500
Kinematik Viskozite, DIN EN ISO 3104 / DIN 51562-1 / ASTM D445 / ASTM D7042, 100°C	Yaklaşık 71 mm²/s	Yaklaşık 110 mm²/s	Yaklaşık 167 mm²/s	Yaklaşık 232 mm²/s
Kinematik Viskozite, DIN EN ISO 3104 / DIN 51562-1 / ASTM D445 / ASTM D7042, 20°C	Yaklaşık 1240 mm²/s	Yaklaşık 1900 mm²/s	Yaklaşık 3000 mm²/s	Yaklaşık 4300 mm²/s
Kinematik Viskozite, DIN EN ISO 3104 / DIN 51562-1 / ASTM D445 / ASTM D7042, 40°C	Yaklaşık 460 mm²/s	Yaklaşık 680 mm²/s	Yaklaşık 1000 mm²/s	Yaklaşık 1500 mm²/s
Viskozite İndeksi, DIN ISO 2909	≥ 230	≥ 250	≥ 260	≥ 270
Bakır Korozyonu, DIN EN ISO 2160, 24 hours, 100°C	1 - 100 - 24 Korozyon Derecesi	1 - 100 - 24 Korozyon Derecesi	1 - 100 - 24 Korozyon Derecesi	1 - 100 - 24 Korozyon Derecesi
Çelik Korozyonu, DIN ISO 7120 / ASTM D665, Yöntem A, 24 Hours, 60°C	Pas Yok	Pas Yok	Pas Yok	Pas Yok
Akma Noktası, DIN ISO 3016	≤ -25 °C	≤ -25 °C	≤ -25 °C	≤ -10 °C
Yaşlanma Davranışı, DIN EN ISO 4263-4 / ASTM D2893, 312 Hours, 95°C, 100°C'de Viskozitede Artış	≤ 6 %	≤ 6 %	≤ 6 %	≤ 6 %
API Aşındırma Yük Kademesi	API GL 5	API GL 5	API GL 5	API GL 5
FAG FE8 Rulman Testi, DIN 51819-3, D-7.5 / 80-80, Kafes Aşınması	≤ 200 mg	≤ 200 mg	≤ 200 mg	≤ 200 mg
FAG FE8 Rulman Testi, DIN 51819-3, D-7.5 / 80-80, Rulman Aşınması	< 5 mg	< 5 mg	< 5 mg	< 5 mg
FZG Aşındırma Testi, DIN ISO 14635-1, Based on Standard, A / 16.6 / 90, Başarısız Yük Kademesi	≥ 12	≥ 12	≥ 12	≥ 12
FZG Aşındırma Testi, DIN ISO 14635-1, A / 8.3 / 90, Başarısız Yük Kademesi	≥ 14	≥ 14	≥ 14	≥ 14
Üretim Tarihinden İtibaren Minimum Raf Ömrü – Açılmamış Orijinal Ambalajında, Serin ve Kuru Yerde, Yaklaşık	36 Ay	36 Ay	36 Ay	36 Ay