Klübersynth BEP 72-82 is based on polyurea and ester oil. The special additives were chosen with a view to preventing premature bearing failure due to material fatigue, which often occurs at high temperatures combined with high speeds and vibrations. The service life of bearings is extended owing to the lubricant's excellent, longterm corrosion protection characteristics.
| Characteristics | Klübersynth BEP 72-82 |
| Article number | 094092 |
| Composition, thickener | polyurea |
| Composition, type of oil | ester oil |
| Colour space | beige |
| Service temperature, lower limit | -40 °C |
| Service temperature, upper limit | 180 °C |
| Density, Klüber method: PN 024, 20°C | approx. 0.9 g/cm³ |
| Worked penetration, DIN ISO 2137 / ASTM D217, 25°C, difference after 100000 double strokes | ≤ 60 0.1 mm |
| Worked penetration, DIN ISO 2137 / ASTM D217, 25°C, lower limit | 250 0.1 mm |
| Worked penetration, DIN ISO 2137 / ASTM D217, 25°C, upper limit | 280 0.1 mm |
| Kinematic viscosity of the base oil, DIN EN ISO 3104 / DIN 51562-1 / ASTM D445 / ASTM D7042, 100°C | approx. 11 mm²/s |
| Kinematic viscosity of the base oil, DIN EN ISO 3104 / DIN 51562-1 / ASTM D445 / ASTM D7042, 40°C | approx. 80 mm²/s |
| Copper corrosion, DIN 51811, 24 h, 100°C | 1 - 100 - 24 corrosion degree |
| SKF-EMCOR, DIN 51802, based on standard, Klüber method: 5 % NaCl solution, 168 h | h ≤ 3 corrosion degree |
| Flow pressure, DIN 51805-2, -40°C | ≤ 1400 mbar |
| Dropping point, DIN ISO 2176 / IP 396 | ≥ 250 °C |
| Speed factor (n x dm) | 1000000 mm/min |
| Water resistance, DIN 51807-1, 3 h, 90°C | ≤ 1 - 90 rating |
| Minimum shelf life from the date of manufacture - in a dry, frost-free place and in the unopened original container, approx. | 36 months |